Dunting In Ceramic

The reasons for that cracking can be many.

Dunting in ceramic.

The first occurs as you cool through the first silica inversion at 1063 degrees f. There are 3 main reasons why cooling dunts occur. Dunting is a fault that can occur during the firing of ceramic articles. Heating dunts can be recognised by rounded.

Dunting is cracking associated with too rapid a cool down of the kiln. Most dunting however is caused in cooling. Dunting generally refers to cracking that occurs in ceramic ware as it is cooled in the kiln. Dunting is a special type of crack which occurs from stresses caused during firing and cooling.

Dunting is cracking associated with a very fast cool down of the kiln. These stresses primarily occur during two critical points of firing called silica inversions which occur at 1063 degrees f 573 degrees c and 439 degrees f 226 degrees c. Dunting is a fault that can occur during the firing of ceramic articles. It is the cracking that occurs in fired ceramic bodies as a result of a thermally induced stress and is caused by a ware cooled too quickly after it has been fired although usually occurring during cooling dunts can also be caused by excessively fast heating rates.

At these inversion points the structure of the silica molecules. According to wikipedia dunting is a fault that occurs during the firing of ceramic articles. These cracks appear as long clean body cracks with sharp edges. They may be vertical horizontal or spiral.

Dunting often exhibits itself as simple hairline cracks but ware can fracture into pieces. If the ware is glazed the glaze edges are sharp.